Fig. 17. (a): Wrec and η as a function of electric field and Wrec comparison of (SrBaPbLaNa)Nb2O6 with other entropic materials of different configurations [36]. (b) Crystal structures of the R (R3c) and T (P4bm) phases with octahedral tilt; The overall energy storage performance of the obtained dielectric ceramics is compared with other work reported [216]. (c) Comparison of energy density and energy storage efficiency of generative learning screened compositions with pristine matrix Bi(Mg0.5Ti0.5)O3 at different breakdown fields. Comparison of energy densities and breakdown fields between original experimental compositions, screened compositions, and the original matrix Bi(Mg0.5Ti0.5)O3 [234].